WO1998009597A2 - Cushioning beads and tablet comprising the same capable of forming a suspension - Google Patents
Cushioning beads and tablet comprising the same capable of forming a suspension Download PDFInfo
- Publication number
- WO1998009597A2 WO1998009597A2 PCT/US1997/015573 US9715573W WO9809597A2 WO 1998009597 A2 WO1998009597 A2 WO 1998009597A2 US 9715573 W US9715573 W US 9715573W WO 9809597 A2 WO9809597 A2 WO 9809597A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- beads
- tablet
- cushioning
- biologically active
- active ingredient
- Prior art date
Abstract
Description
Claims